AMS5662

COMMON NAMES:

Alloy 718

UNS N07718

FORM & USE:

AMS5662

AMS5662 is a corrosion and heat resistant nickel alloy. We stock round bar in the annealed condition. The material is typically used in aerospace, oil and gas and general engineering applications which require high resistance to creep and stress rupture up to 704oC and oxidation resistance up to 982oC. The material can be weld d. After forming or welding, the material can be precipitation heat treated to meet AMS5663.

We supply material in the hot finished, solution he at treated, and descaled, ground or turned condition.

GENERAL:

Tolerances in accordance with AMS2261.

Bars are not cut from plate.

SIZES STOCKED:

9.525 mm diameter – 200 mm diameter.

CHEMISTRY:

CMnSiPSCrNiMoNb (Cb)Ti
< 0.08< 0.35< 0.35< 0.015< 0.01517.00 – 21.0050.00 – 55.002.80 – 3.304.75 – 5.500.65 – 1.15
AlCoBCuPbBiSeFe
0.20 – 0.80< 1.00< 0.006< 0.30< 0.0005 (5ppm)
< 0.00003 (0.3ppm)
< 0.0003 (3ppm)
Balance

MELTING PRACTICE:

Material is multiple melted using consumable electrode practice in the remelt cycle OR is induction melted under vacuum. If consumable electrode remelting is not performed in vacuum, electrodes which have been produced by vacuum induction are used for remelting.

HEAT TREATMENT:

Solution heat treated by heating to 941°C – 1010°C, holding at temperature for a time commensurate with cross-sectional thickness, and cooling in air (faster methods permitted).

Pyrometry in accordance with AMS2570.

FINISH:

Material is supplied hot finished, annealed, ground or turned.

MATERIAL PROPERTIES:

Grain Size:

Determined in accordance with ASTM E112.

Up to 58cm2 in cross-sectional area – ASTM No. 5 or finer (up to 20% of material permitted to have average grain size of ASTM No 3 to 5).

From 58cm2 to 503cm2 cross-sectional area – ASTM No. 4 or finer (up to 20% of material permitted to have average grain size of ASTM No 2 to 4).

Microstructure:

Product is free from Laves phase. Banding of acicular phase and the amount of acicular phase are determined by the purchaser. If not specified, material is sold as is.

Tensile Properties:

Determined in accordance with ASTM A370 on specimens taken in the longitudinal direction from product less than 254 mm in diameter. The specimen for AMS5663 is aged in accordance with the ageing cycle before testing.

 Minimum Tensile StrengthMinimum Yield strength at 0.2% OffsetMinimum Elongation in 2” or 4dMinimum Reduction of AreaHardness
KsiKsi%%
Solution Annealed at room temperature
<277 HB
AMS5663 capability at room temperature
Longitudinal up to 254 mm dia1851501215<331 HB
Transverse up to 127 mm dia18015068<331 HB
Transverse from 127 mm – 254 mm dia18014568<331 HB
AMS 5663 capability at 1200°F (649°C)
Longitudinal up to 127 mm dia1451251215
Longitudinal 127 mm dia up to 254 mm dia1451221215
Transverse up to 127 mm dia14012568
Transverse from 127 mm – 254 mm dia14012268

A “-“ indicates no requirement for the property.

The AMS standard states that material shall not be rejected on hardness if the tensile properties are acceptable.

Stress Rupture Properties:

AMS5663 capability Performed in accordance with ASTM E292 (notched specimens and smooth-and-notched specimens) or ASTM E139 (smooth specimens).

ASTM E292: a notched specimen at 649oC with a load sufficient to produce an axial stress of 100 ksi (or higher) is applied continuously. Stress rupture to occur in not less than 23 hours. Test is continued to rupture without change of load. Elongation after rupture (measured at room temperature) is not less than 4% in 4D for product 127 mm and under in diameter.

Incremental loading – after 23 hours a further +6 ksi load can be applied at 8 hourly intervals until rupture.

Production, distribution, and procurement of metal stock complies with AMS6279.

Full material traceability, with anti-counterfeit measures, is maintained at all times, and full certification is provided, including producer’s name and country where the material was melted.

We welcome your enquiries. To discuss your requirements, or for a quotation please telephone 0114 349 3595, email sales@broder-aerospace.com or send an enquiry through the contact page.